Analysis of the sintering process of 316l – Hydroxyapatite composite biomaterials
cytuj
pobierz pliki
RIS BIB ENDNOTEWybierz format
RIS BIB ENDNOTEData publikacji: 08.02.2016
Czasopismo Techniczne, 2015, Mechanika Zeszyt 3-M (21) 2015, s. 79 - 82
https://doi.org/10.4467/2353737XCT.15.178.4383Autorzy
Analysis of the sintering process of 316l – Hydroxyapatite composite biomaterials
The 316L-hydroxyapatite biocomposites were produced by the powder metallurgy technology. The properties and microstructure of these materials are affected by the chemical composition of the powders mixture and the sintering temperature. The sintering temperature of 1240°C and hydroxyapatite addition in an amount of 3% of mass obtained the highest density and hardness and smaller open and closed porosity. Hydroxyapatite addition to austenitic stainless steel modified sintering behaviour. During heating the thermal decomposition of hydroxyapatite took place, which led to the formation of a CaO phase. However, phosphorus diffused into the austenitic matrix and was involved in the eutectic transformation.
Informacje: Czasopismo Techniczne, 2015, Mechanika Zeszyt 3-M (21) 2015, s. 79 - 82
Typ artykułu: Oryginalny artykuł naukowy
Tytuły:
Instytut Inżynierii Materiałowej, Wydział Mechaniczny, Politechnika Krakowska
Instytut Inżynierii Materiałowej, Wydział Mechaniczny, Politechnika Krakowska
Publikacja: 08.02.2016
Status artykułu: Otwarte
Licencja: Żadna
Udział procentowy autorów:
Korekty artykułu:
-Języki publikacji:
AngielskiLiczba wyświetleń: 1552
Liczba pobrań: 1428