Marcin Górski
Czasopismo Techniczne, Volume 9 Year 2019 (116), 2019, s. 107 - 118
https://doi.org/10.4467/2353737XCT.19.100.10882The main goal of the research was to check the influence of different factors on the mechanical behaviour of the fluidised bed combustion (FBC) fly ash-based geopolymer. Tests have shown that the increasing the proportion of sodium silicate to sodium hydroxide causes a decrease of compressive strength and an increase of flexural strength. The addition of aggregate significantly increased flexural strength but decreases compressive strength. Samples cured at higher temperatures obtained higher strength. Finally, it was concluded that taking into account the mechanical behaviour, FBC fly ash-based geopolymer can be treated as an alternative building material; however, its strength is lower than a metakaolin-based geopolymer made of the same mixture composition.
Keywords: FBC fly ash, geopolymer, curing conditions, compressive strength, flexural strength
Streszczenie
Głównym celem badania było wyznaczenie wpływu wybranych czynników na wytrzymałość geopolimeru bazującego na fluidalnym popiele lotnym. Badanie wykazało, że wzrost stosunku masowego szkła wodnego do wodorotlenku sodu powoduje spadek wytrzymałości na ściskanie i wzrost wytrzymałości na rozciąganie geopolimeru. Dodatek kruszywa (piasku) powoduje natomiast wzrost wytrzymałości na rozciąganie i spadek wytrzymałości na ściskanie. Odnotowano, że próbki dojrzewające w wyższych temperaturach uzyskują wyższą wytrzymałość. Na podstawie wykonanych badań stwierdzono, że biorąc pod uwagę wytrzymałość badanego geopolimeru, można uważać go za alternatywny materiał budowlany. Wytrzymałość badanego geopolimeru jest jednak niższa od wytrzymałości geopolimeru na bazie metakaolinu.