Anna Kufel
Czasopismo Techniczne, Volume 1 Year 2019 (116), 2019, s. 187 - 195
https://doi.org/10.4467/2353737XCT.19.013.10053Composites based on a polypropylene matrix with coffee ground powder, wood flour and tuff of a mass weight of 12.5wt% were produced by the method of injection moulding. Tests of tensile and bending strength properties were carried out and Charpy impact was determined at three temperatures: -24°C, 22°C and 80°C. Scanning electron microscopy (SEM) images were taken to assess the effects of reinforcement and homogenization of mixtures and to determine the characteristics of the microstructure. Composites with 12.5wt% coffee ground powder, wood flour and tuff were characterized by an increase the elastic modulus. Tensile strength slightly decreased for composites with ground coffee grains and tuff.
Kompozyty na osnowie polipropylenu modyfikowane naturalnymi napełniaczami w celu zwiększenia sztywności
Streszczenie
Wytworzono kompozyty na osnowie polipropylenu modyfikowane zmieloną kawą, mączką drzewną oraz tufem w ilości masowej 12.5%. Kompozyty zostały wytworzone metodą formowania wtryskowego. Została wykonana statyczna próbę rozciągania oraz zginania, a także próba udarności w trzech temperaturach eksploatacji: -24°C, 22C°, 80°C. W celu określenia charakterystyki i zbadania wpływu wzmocnienia oraz homogenizacji mieszaniny wykonano zdjęcia na skaningowym mikroskopie elektronowym. Kompozyty z 12.5wag.% zawartością kawy, mączki drzewnej lub tufu charakteryzują się zwiększonym modułem sprężystości oraz nieznacznym spadkiem sztywności dla kompozycji z kawą i tufem.